| Quantity | Price per Unit |
|---|---|
| 1-10 Sheets | £89.37 |
| 10-20 Sheets | £86.62 |
| 20+ sheets | £PoA |
Type the quantity required of this material and click “Add to Quote”
Materials currently in your list to quote:
Simply complete a few fields below and we will get back to you shortly!
Finish Type / Pattern:
Smooth
Thickness:
9.15mm (±0.3)
Width:
1220mm
Height:
2440mm
(Cut to Size options available!)
Recycled thermoplastic sandwich panel, thermoplastic core fused to thermoplastic skin laminate with a matte, smooth surface finish for easy decal adhesion.
| Product | Thickness (mm) | Weight (kg/m2) | Density (g/cm3) | Colour |
| RecoreLite® | 9.15±0.3 | 3.9 | 0.428 | Black |
| Dimension (mm) | Tolerance (mm) | |
| Width | 1220 | ±3 |
| Length | 2440 | ±3 |
| Material | Anti-Slip Rating (Dry) | Anti-Slip Rating (Wet) | |
| Smooth | rABS | n/a | n/a |
Adhesive Bonding (Cyano-acrylates, Silicates) Welding
Screwing Drilling Riveting
Cutting (hand-held or mechanical saw) Routing
| Property | Method | Unit | Result |
| Tensile Strength, Yield | ISO 37:2017 | MPa | 37.1 |
| Elongation, Yield | ISO 37:2017 | % | 2.7 |
| Flexural Modulus | ISO 178 | GPa | 2.02 |
| Izod Impact Strength | ISO 180 | kJ/m2 | 36.3 |
| Melt Flow Index | ISO 1133 | g/10min | 1.93 |
Thermal Properties of raw Material*
| Property | Method | Unit | Result |
| Melting Point | ISO 3146:2022 | °C | 260 |
| Heat Deflection
Temperature at 0.46 MPa |
ISO 75-2 | °C | 90.5 |
| Heat Deflection
Temperature at 1.8 MPa |
ISO 75-2 | °C | 89.6 |
| Flash Point | ASTM D1929 B | °C | 349 |
| Auto Ignition Temperature | ASTM D1929 B | °C | 508 |
| Thermal Expansion
coefficient |
ISO 11359 | mm/m°C |
0.0738 |
| Property | Method | Unit | Result |
| Flexural Strength | ISO 178 | Nmm | 7.5×104±0.2×104 |
| Max Bending Moment | ISO 178 | N | 293±10 |
| Compression Strength | ISO 604 | MPa | 2.7±0.3 |
| Wheel Compression, Limit
Load (Ø80x25mm) |
Internal | kg | <60 |
* Values taken from MatWeb database for ABS sheet.
**Average values taken in house with 3 point bending and flat platen compression. Flexural Strength calculated as a bending moment per mm of sample width.
Resistant to aqueous acids, alkalis, hydrochloric and phosphoric acids as well as animal, vegetable, and mineral oils. Do not use with aromatic hydrocarbons, glacial acetic acid, or carbon tetrachloride. It is attacked by concentrated sulphuric and nitric acid.
Clean with water or with Isopropyl Alcohol, DO NOT clean with Acetone based products.
RecoreLite® is a non-biodegradable product.
Hereby, we confirm that our products are based on rABS which is 100% recyclable and is widely recycled.
RecoreLite® can be reground, and re-pelletised ready for re-extrusion (currently done on our own production waste).
We offer a free take back scheme for this product if you are unable to recycle it yourself, please contact us for more information.